ASTM A213 T9/T11/T22/T91 Alloy na igwe anaghị agba nchara maka igwe ọkụ na ndị na-agbanwe ọkụ

Ebe Tubes ndị a na-arụ ọrụ kacha mma (na ihe kpatara na-ejiri igwe anaghị agba nchara)

Igwe ọkụ ọkụ, HRSG, igwe ọkụ petrochemical na kọmpat ndị na-agbanwe ọkụ na-adabere na ASTM A213/SA213 tubes enweghị nkebi. Mgbe chloride - na-ebu condensate, usoro mmiri na-ekpo ọkụ ugboro ugboro, ma ọ bụ ihe na-achọsi ike ịdị ọcha dị na tebụl,austenitic igwe anaghị agba nchara (TP usoro)na-arịgo karịa chrome{0}moly ferritic grades ekele maka corrosion izugbe kacha elu na nguzogide ọgbaghara, imecha nke ọma nke ọma, yana nhicha dị mfe. Okpomọkụ- dị elu, ọrụ akọrọ nke nwere oke ihe na-akpụ akpụ ka na-edobe yaT{0}} akara ulena-egwu - karịsịa maka ụlọ akụ superheater na reheater.

Ọnọdụ eji eme ihe:

Igwe anaghị agba nchara (TP304/304H, TP316L/316H, TP321/321H, TP347/347H): ndị na-agbanwe ọkụ, ngwugwu condenser, nri{8}}ihe ọkụ mmiri, corrosive or cyclic-ọrụ mmiri mmiri.

Alloy ferritic (T9, T11, T22, T91): ngalaba na-ekpo ọkụ ọkụ ọkụ/ọkụ ọkụ na nkụnye eji isi mee ebe ogologo - ike creep na-achị.

astm a213 sa213 seamless tubing bundles t11 t22 t91-octal pipe chrome moly boiler tubing sa213 t22 t91 packed for shipment-octal pipe

Ịhọrọ igwe anaghị agba nchara vs. Chrome -Moly: Ụzọ bara uru

Ụzọ dị mfe isi dozie mkpebi ahụ bụ maapụọkara + okpomọkụ + ebumnuche ndụruo ezinụlọ ọkwa.

Tebụl 1 - Atụmatụ nhọrọ ngwa ngwa

Atụmatụ ọrụ	Ezinụlọ TP igwe anaghị agba nchara (nke a na-ahụkarị)	Ezinụlọ Ferritic T (nke a na-ahụkarị)
Chlorides / okirikiri mmiri-akọrọ / ịdị ọcha	TP316L/316H; TP304/304H ma ọ bụrụ na chloride dị ala	Ọ bụghị ọkachamma
Njikwa mmetụta na oke okpomọkụ	TP321/321H (Ti- kwụsiri ike); TP347/347H	-
Oke oke na-akpụ akpụ (gas kpọrọ nkụ, na-ekpo ọkụ nke ukwuu)	TP347H/321H n'ọnọdụ ahọpụtara	T91 > T22 > T11 ≈ T9
Ihe ize ndụ kacha nta nke itinye n'ọrụ mmiri osimiri	TP316L (Mo{1})	-
Ọnụ - ịrụ ọrụ nke ọma na ọrụ ọkụ adịghị oke	TP304/304H	T11/T22 (mgbe corrosion dị nro)

Nkọwapụta ọrụ na-emeri mgbe niile; Tebụl bụ ụzọ mkpirisi maka nyocha mbụ.

Ọkwa igwe anaghị agba nchara na nlele (usoro TP)

Tebụl 2 - Nhọrọ igwe anaghị agba nchara n'okpuru A213

Ọkwa	Isi ihe dị na kemistri	Kedu ihe ọ dị mma	Ngwa a na-ahụkarị
TP304 / 304H	~18Cr-8Ni (H=oke ikuku ikuku dị elu)	Ngwa ngwa ngwa; elu dị ọcha; ezigbo mmepụta ihe	Condenser/okpomọkụ{0}} ngwugwu ihe ngbanwe, ọkụ
TP316L / 316H	Na-agbakwụnye ~ 2–3% Mo; L=obere C; H=dị elu - okpomọkụ	Nguzogide ntupu / mgbape ka mma vs 304/304H	Mmiri mmiri - dị n'akụkụ jụrụ oyi, mgbasa ozi chloride
TP321 / 321H	Nke - kwadoro	Njikwa mmetụta na okpomọkụ dị elu	Igwe ọkụ dị elu, ndị na-agbanwe okpomọkụ dị elu
TP347 / 347H	Nb- kwadoro	Yiri 321; windo nkwụsi ike siri ike	Igwe ọkụ / igwe ọkụ na-eji igwe igwe ọkụH{0}ka akara ule gbagoro elu{1}}ike okpomọkụ; L- akara ule lekwasịrị anya weldability na iguzogide mmetuta na ọrụ mmiri.

Ferritic Alloy "T" akara ule na Context

Tebụl 3 - Ebe T9, T11, T22, T91 dabara adaba

Ọkwa	Echiche (ọnụ ọnụ)	Echiche ike (ọkụ)	Ọrụ a na-ahụkarị
T11	~1.25Cr-0.5Mo	Ntọala	Ọkụ ọkụ ọkụ ọkụ ọkụ{1} na-agafeghị oke{0}}
T22	~2.25Cr-1Mo	↑ vs T11	Ụlọ akụ dị ọkụ; ọnụ - oke nrara nke ọma
T9	~9Cr-1Mo (ferritic)	Otu egwu yiri T22	Họrọ ọrụ ọkụ na mpaghara mgbanwe
T91	9Cr-1Mo-V-Nb (Martensite na-ewe iwe)	Otu kachasị elu	Akụkụ ihe ọkụ ọkụ ọkụ/ọkụ ọkụ na-ekpo ọkụ nke ukwuu

Chemistry Snapshots (ntụgharị aka)

Tebụl 4 - Igwe anaghị agba nchara Austenitic (usoro TP, wt.%)

Ọkwa	C (L/H)	Cr	Ni	Mo	Stabilizer
TP304/304H	Ihe na-erughị ma ọ bụ hà nhata 0.035 / 0.04–0.10	~18–20	~8–11	-	-
TP316L/316H	Ihe na-erughị ma ọ bụ hà nhata 0.035 / 0.04–0.10	~16–18	~10–14	~2.0–3.0	-
TP321/321H	Ihe na-erughị ma ọ bụ hà nhata 0.035 / 0.04–0.10	~17–19	~9–13	-	Ti
TP347/347H	Ihe na-erughị ma ọ bụ hà nhata 0.035 / 0.04–0.10	~17–19	~9–13	-	Nb/Ta

Tebụl 5 – Ferritic alloy (usoro T, wt.%)

Ọkwa	C (ụdị)	Cr (ụdị)	Mo (ụdị)	V/Nb/N (mgbe ọdabara)
T11	Ihe na-erughị ma ọ bụ hà nhata 0.12	~1.0–1.5	~0.44–0.65	-
T22	Ihe na-erughị ma ọ bụ hà nhata 0.15	~1.9–2.6	~0.87–1.13	-
T9	Ihe na-erughị ma ọ bụ hà nhata 0.15	~8–10	~0.9–1.1	-
T91	0.08–0.12	~8–9.5	~0.85–1.05	V, Nb, N obere mgbakwunye

Gaa na ASTM A213/SA213 kacha ọhụrụ maka oke ọchịchị na nnabata nyocha ngwaahịa.

Mechanical & High{{0}Okpomọkụ akara (opekempe na ụlọ okpomọkụ)

Tebụl 6 - Opekempe egosi (lelee koodu/ọkọlọtọ dị ugbu a)

Ezinụlọ / Ọkwa	Tensile min	Mpụta min	Ogologo oge min
Austenitic (dịka, TP304/316L)	≈ 515 MPa (75 ksi)	≈ 205 MPa (30 ksi)	≈ 35%
TP321/347 (H akara ule)	≈ 515 MPa	≈ 205 MPa	≈ 30–35%
T11/T22	≈ 415 MPa	≈ 205 MPa	≈ 20%
T91	≈ 585 MPa	≈ 415 MPa	≈ 20%

Ihe ndetu nrụpụta - Naanị enweghị nkebi (A213 Oke)

Ụzọ:na-ekpo ọkụ - agwụchachaa wee jụọ oyi{1}} agwụchala nha; igwe anaghị agba nchara -annealed napickled/passivatedmaka ID dị ọcha.
Ọgwụgwọ okpomọkụ:austenitic igwe anaghị agba nchara{0}}ihe ngwọta anneal + ngwa ngwa jụụ; T91-normalize & iwe (kwa ụdịdị); T11/T22-normalizing ma ọ bụ subcritical ọgwụgwọ dị ka akọwapụtara.
Elu & ịdị ọcha:igwe anaghị agba nchara tubing na-enye oge niile na NJ dị ala maka nnyefe ọkụ dị mma ma dị ọcha{1} n'ime{2} usoro usoro.
Geometry:nnabata OD/ọkpụrụkpụ siri ike na nkwụ ọtọ na-enyere aka ikpokọta mgbakọ na tube -na{1}}ịgbado ọkụ tube.
Ị - na-ehulata:nke a na-enyekarị maka ikpo ọkụ igwe anaghị agba nchara{0}}nwere igwe na-agbanwe agbanwe nwere radi agbagọ na-achịkwa yana enyemaka nrụgide mgbe achọrọ ya.

Nnwale & Nyocha I Kwesịrị Ezipụta

Tebụl 7 - Ihe ndị a na-achọkarị n'okpuru A213 (ọrụ - dabere)

Ihe	Usoro TP igwe anaghị agba nchara	T{0}usoro (T11/T22/T91)
Nnwale eletriki Hydrostatic ma ọ bụ NDE	Amanyere iwu (otu ma ọ bụ nke ọzọ)	Amanyere iwu (otu ma ọ bụ nke ọzọ)
Eddy current / ultrasonic (NDE)	Ọtụtụ mgbe akọwapụtara maka mkpuchi 100%.	Ọtụtụ mgbe akọwapụtara maka mkpuchi 100%.
Nnwale flattening/flare/flange	Dị ka akọwapụtara na A213	Dị ka akọwapụtara na A213
Nha ọka (austenitic)	Achọrọ ebe ọdabara	-
Nnwale corrosion intergranular (IGC)	Site n'usoro (dịka ASTM A262 ụzọ)	-
njikwa ike ike	Na-emekarị ozi	Dị oke mkpa maka T91 kwa usoro
PMI & akwụkwọ	PMI na ngwugwu; ngwugwu MTC zuru oke	PMI na ngwugwu; ngwugwu MTC zuru oke

Nnweta akụkụ (Ntụaka Ọkụ Octal)

Tebụl 8 - envelopu ọkọnọ a na-ahụkarị (ọrụ{1} akọwapụtara)

Oke	Usoro TP igwe anaghị agba nchara	T{0}usoro (T11/T22/T91)
Dayameta dị n'èzí	~ 12.7-114.3 mm (½ na-4½ n'ime)	Oke nso
Ọkpụrụkpụ mgbidi	~ 1.24-12.7 mm (otu oge / eserese)	~ 2-16 mm (mgbidi dị arọ dị.)
Ogologo	Ruo 12 m ahụkarị; bee -ruo{2}} ogologo	Ruo 12 m ahụkarị
Emecha	Pickled/passivated, a na-egbu maramara na req	Emecha nke ọma/iwe ọkụ
tube na-agwụ	Akwụsị larịị; tube -ka -tubesheet prep	Akwụsị larịị; na-atụgharị ma ọ bụrụ na achọrọ

Ndepụta ndenye iwu (Ihe ị ga-etinye na mpempe akwụkwọ data)

Ọkwa na ọnọdụ: TP304 / 316L / 321/347 (L / H dị mkpa) ma ọ bụ T11 / T22 / T91 na chọrọ okpomọkụ ọgwụgwọ.
Akụkụ: OD, mgbidi, ịkpụ ogologo; Na {{0}na-ehulata radis na nkwado ụkwụ ma ọ bụrụ na ọdabara.
Ọgwụgwọ okpomọkụ & elu: ngwọta anneal + pickling/passivation (igwe anaghị agba nchara); normalize/iwe ọkụ (dị ka ọdabara).
Atụmatụ NDE: ule hydrostatic ma ọ bụ eletrik; 100% eddy ugbu a / UT ma ọ bụrụ na achọrọ; njirisi nnabata.
Njikwa mmebi: Nnwale IGC maka akara ule kwụsiri ike ma ọ bụrụ na akọwapụtara ya; oke chloride; ihicha protocol.
Akwụkwọ: MTC kwa EN 10204 (dịka, 3.1), traceability, mbukota, akara.
Ndị nke atọ-: ịgba ama/nyochadị na arịrịọ(BV, SGS, wdg).

FAQ

Q1: Kedu otu m ga-esi họrọ n'etiti akara TP igwe anaghị agba nchara na chrome{1}}moly T n'okpuru ASTM A213/SA213?
A1:Jiri akara TP maka ọrụ mmiri/uyi ma ọ bụ chloride na mkpa ịdị ọcha; jiri T grades mgbe akọrọ dị elu-okpomọkụ ike na-akpụ akpụ bụ isi ọkwọ ụgbọala.

Q2: Gịnị bụ ihe dị iche n'etiti SA213 T11, T22, na T91 tubing?
A2:T11 bụ ntọala maka okpomoku na-agafeghị oke, T22 na-agbakwunye oke mkpụbelata maka ngalaba dị ọkụ, yana T91 ka a na-eji maka ọrụ kacha elu{3}}okpomọkụ superheater/reheater.

Q3: Kedu nyocha na akwụkwọ m ga-arịọ maka ASTM A213/SA213 tubing?
A3:Rịọ maka ule eletriki hydrotest ma ọ bụ NDE, 100% eddy current/UT ma ọ bụrụ na achọrọ ya, PMI, yana EN 10204 3.1 MTC zuru oke nwere ndekọ ọgwụgwọ{2}.

Kpọtụrụ ugbu a